Formation of water-impermeable crust on sand surface using biocement

Вантажиться...
Ескіз

Дата

2011

ORCID

DOI

Науковий ступінь

Рівень дисертації

Шифр та назва спеціальності

Рада захисту

Установа захисту

Науковий керівник

Члени комітету

Видавець

Анотація

This paper examines the feasibility of using calcium-based biocement to form an impermeable crust on top of a sand layer. The biocement used was a mixture of calcium salt, urea, and bacterial suspension, which hydrolyzed urea with production of carbonate and an increase of the pH level. Applying 0.6 g of Ca per cm2 of sand surface, the permeability of the biocemented sand can be reduced from 10−4 m/s to 1.6•10−7 m/s (or 14 mm/day) due to formation of the crust on sand surface. The rupture modulus (maximum bending stress) of the crust was 35.9 MPa, which is comparable with that of limestone. The formation of a water-impermeable and high strength crust layer on sand surface could be useful for the construction of aquaculture ponds in sand, stabilization of the sand dunes, dust fixation in the desert areas, and sealing of the channels and reservoirs in sandy soil.

Опис

Ключові слова

bending strength, calcium carbonate, permeability, scanning electron microscopy, опір на вигин, карбонат кальцію, електронний скануючий мікроскоп, водопроникливість, сопротивление на изгиб, карбонат кальция, электронный сканирующий микроскоп, водопроницаемость, кафедра біотехнології і мікробіології

Бібліографічний опис

Formation of water-impermeable crust on sand surface using biocement / V. Stabnikov, M. Naemi, V. Ivanov, J. Chu // Cement and Concrete Research. - 2011. – v. 41, № 11. – Р. 1143–1149.

Зібрання